Volume 22 Preprint 39

Improve Corrosion Resistant and Corrosion Fatigue Cracking Performance on AISI 304 by Shot Peening Process as Alternative Biomaterials

Bambang Hari Priyambodo, Viktor Malau, Priyo Tri Iswanto, Lilik Dwi Setyana, Sugeng Slamet and Yani Kurniawan.

Keywords: AISI 304, Bovine Serum, Corrosion, Fatigue, Shot Peening.

Generally, component failure starts at the surface of the biomaterials. Therefore it is necessary to obtain a surface treatment of physical and mechanical properties better. This study investigated the effect of hardness, corrosion rate and fatigue cracking on AISI 304 by shot peening process. Shot peening was performed with 0.5 mm diameters of steel balls and 20 minutes duration. The hardness of those balls is 40-50 HRC. Shot peening pressure was varied as follows 7, 8 and 9 Bar. Vickers hardness test was carried out 10 grams of a load for 10 seconds. The corrosion rate and the corrosion fatigue test were conducted in a bovine serum solution. The results show shot peening process improved the evaluated parameters. This value was about 2 times of hardness for 248 VHN, decreased 1/3 times of corrosion rate for 0.378 mpy, and reduced the rate of cracking at less than about 1 MPa√m load. The optimum value was at 9 Bar of shot peening pressure.

Because you are not logged-in to the journal, it is now our policy to display a 'text-only' version of the preprint. This version is obtained by extracting the text from the PDF or HTML file, and it is not guaranteed that the text will be a true image of the text of the paper. The text-only version is intended to act as a reference for search engines when they index the site, and it is not designed to be read by humans!

If you wish to view the human-readable version of the preprint, then please Register (if you have not already done so) and Login. Registration is completely free.

Review of "Application of the Electrochemistry Noise Technology to the Evaluation of the Corrosion Inhibitor" by Jun Cui, Yuansheng Pei While this paper on the application of EN techniques to the study of inhibitor performance is potentially useful, the paper suffers from a number of weaknesses: •The English is poor, such that it is often unclear and in at least one case says the opposite of what I believe is intended. •The description of experimental and data analysis procedures is inadequate. •There are questions about the quality of the measured data and the accuracy of some of the data presented. It may be possible to produce a revised paper that is suitable for publication, but only if it can be demonstrated that the measured data are valid. L44"However, the weight loss experiment consumes a large amount of materials owing to the non-reusable of the metal substrate;" unless the material is extraordinarily expensive this is a very minor problem compared to the other costs involved. L50 "in-suit" presumably "in-situ" is intended. L65"However, rare studs apply EN technology to evaluate the passivation behavior of the corrosion inhibitor." - while there may be relatively few studies using EN on inhibited systems, there have been some, and these should be mentioned. L74"a controlled-release inhibitor" this is an inadequate description of the inhibitor chemistry. L100"44% of epoxy value" what does this mean? L102"polisher powder" inadequate description. L109I believe the Autolab potentiostat does not have anti-aliasing filters that can be adjusted to be appropriate for the sampling frequency in use, so there is a significant risk that the measured data are contaminated by aliasing. The validity of the measured EN needs to be confirmed (e.g. by following the procedure in "Guideline for an assessment of electrochemical noise measurement devices", S. Ritter, F. Huet and R.A. Cottis, Materials and Corrosion-Werkstoffe Und Korrosion, Volume: 63, Issue: 4, Pages: 297-302, 2012). L116"five-order fitting method" presumably this really means subtraction of a fifth order polynomial, but the significance of this remains unclear, since there is no mention of the time record duration to which this trend removal was applied. L126More information needed on EIS parameters, particularly number of frequencies per decade and overall measurement time. L146"an acceptable passivation performance was obtained until the total boron concentration over 100 mg L-1" should this actually say "... was not obtained ..."? L147It appears that the objective of the test procedure on the controlled release inhibitor was to test in reasonably constant inhibitor concentration, in which case why was a controlled release inhibitor used? L28530 days is hardly 'long-term' in a real application. L395"shot noise". Figure 3The normalization of the current and potential signals with respect to area makes no sense at all. For absolute values of current and potential it is reasonable to report current per unit area and potential independent of area, but for EN the effect of area is less clear, so it is best just to report coupling current and potential (see "The Interpretation of Electrochemical Noise Data", R.A.Cottis, Corrosion, 27, 3, 265-285 (2001)). It is also unclear what is actually being plotted - are they the 'raw' potential and current (this seems unlikely as the signals display little short-term variation) or the results after trend removal or some other statistical treatment such as standard deviation? Figures 4, 9, 13Why is 1/Rn plotted in 4 and Rn or Rp in 9 and 13 - this is just confusing? Also the 1/Rn values in 4 seem completely incompatible with the Rn values in 9 and the Rp values in 13