Mairaj Ahmad
Schlüsselwörter: Nanocomposites, Nitinol, Phase Transformation, Vicker, Corrosion
Zusammenfassung:
<p>Titanium-nickel pre-alloyed particles were reinforced with silica
particles of constant volume percent with sizes varying as proceeding 50, 100,
250, and 500 nm. The weighed compositions were mixed in a planetary ball mill,
followed by compaction via uniaxial compression of 50 MPa. The resultant green
pellets were sintered in an argon atmosphere at 1223K for a period of 4 hrs.
Following that, by using EDM the composite pellets were sectioned, soldered and
cold mounted. Microstructure analysis was performed optical microscopy, micro
Vickers hardness testing for mechanical evaluation followed by potentiodynamic
polarization and electrical impedance spectroscopy (EIS) for electrochemical evaluation
whereas the effect of particle size at constant volume on the densification was
determined via the Archimedes Principle. The reinforcement showed increasing
hardness and increase in phase distribution in addition to the effect
complimented by the transformation of silica whereas electrochemical evaluation
was affected by both reinforcement and phase distribution.<br></p>
Da Sie nicht beim Journal angemeldet sind, ist es nun unsere Richtlinie, eine 'Nur-Text'-Version des/der preprint anzuzeigen. Diese Version wird durch Extraktion des Textes aus der PDF- oder HTML-Datei erstellt, und es ist nicht garantiert, dass der Text ein originalgetreues Abbild des Textes des Artikels ist. Die Nur-Text-Version soll als Referenz für Suchmaschinen bei der Indexierung der Website dienen und ist nicht dafür gedacht, von Menschen gelesen zu werden!